Stainless 304/304H
General
One of the most widely used and oldest of the stainless steels. This was originally called 18-8 which stood for its chromium and nickel content. It possesses an excellent combination of strength, corrosion resistance and fabricability
Chemical Composition
|
|
C |
Mn |
Ni |
Si |
Cr |
S |
P |
Fe |
|
|
|
|
Min % |
– |
– |
8.00 |
– |
18.00 |
– |
– |
Bal. |
|
|
|
|
Max % |
0.08 |
2.00 |
10.50 |
1.00 |
20.00 |
0.03 |
0.045 |
– |
|
|
|
|
Other Elements |
|||||||||||
Mechanical Properties
|
|
MPA |
% |
|
Tensile Strength. |
515 |
|
|
Yield Strength (0.2% offset) |
205 |
|
|
Elongation in 2” (50mm) or 4D |
|
40 |
|
Reduction of Area, min |
|
|
|
|
|
|
|
Hardness |
92 HRB |
|
Alternative Designations
|
AFNOR Z7CN 18-09 AISI 304 AMS 5501 AMS 5513 AMS 5560 AMS 5563 AMS 5564 AMS 5565 AMS 5566 AMS 5567 AMS 5639 AMS 5697 ASTM A167 ASTM A182 ASTM A193 (304, B8, B8A) ASTM A194 ASTM A213 ASTM A240 ASTM A249 ASTM A269 ASTM A270 ASTM A271 ASTM A276 ASTM A312 ASTM A313 ASTM A314 ASTM A320 ASTM A336 ASTM A358 ASTM A368 ASTM A376 ASTM A409 ASTM A430 ASTM A473 ASTM A478 ASTM A479 ASTM A492 ASTM A493 ASTM A511 ASTM A554 ASTM A580 ASTM A632 ASTM A666 ASTM A688 ASTM A793 ASTM A813 ASTM A814 ASTM A851 DIN 1.4301 MIL A-23196 MIL S-23195 MIL S-23196 MIL S-27419 MIL S-5059 MIL T-5695 MIL T-6845 MIL T-8504 MIL T-8506 QQ S763 QQ S766 UNS S30400
|
The data contained in this publication is for informational purposes only and may be revised at any time without prior notice. The data is believed to be accurate and reliable, but Hague Fasteners Limited makes no representation or warranty of any kind (express or implied) and assumes no liability with respect to the accuracy or completeness of the information contained herein. Although the data is believed to be representative of the product, the actual characteristics or performance of the product may vary from what is shown in this publication. Nothing contained in this publication should be construed as guaranteeing the product for a particular use or application.