Hastelloy B3
General
HASTELLOY B3 alloy is suitable for use in all applications previously requiring the use of HASTELLOY B-2 alloy. Like B-2 alloy, B-3 is not recommended for use in the presence of ferric or cupric salts as these salts may cause rapid corrosion failure. Ferric or cupric salts may develop when hydrochloric acid comes in contact with iron or copper
Chemical Composition
|
Ni |
Cr |
Mo |
Mn |
Fe |
Si |
C |
Al |
W |
Co |
Ti |
Nominal |
65.00 min. |
1.50 min |
28.50 min. |
3.00 max |
1.50 min |
0.10 max |
0.01 max |
0.50 max |
3.00 max |
3.00 max |
0.20 max |
|
W 3.00 max |
Mechanical Properties (typical)
|
MPa |
% |
Tensile Strength. |
890 |
|
Yield Strength (0.2% offset) |
385 |
|
Elongation in 2” (50mm) or 4D |
|
60.4 |
Reduction of Area |
73 |
|
|
|
|
Hardness |
– |
|
Alternative Designations
Alloy B3, UNS N10675, W.Nr 2.4600, Hastelloy B3, NiMo29Cr |
The data contained in this publication is for informational purposes only and may be revised at any time without prior notice. The data is believed to be accurate and reliable, but Hague Fasteners Limited makes no representation or warranty of any kind (express or implied) and assumes no liability with respect to the accuracy or completeness of the information contained herein. Although the data is believed to be representative of the product, the actual characteristics or performance of the product may vary from what is shown in this publication. Nothing contained in this publication should be construed as guaranteeing the product for a particular use or application.