Stainless steel 310, is a medium carbon austenitic, generally used in high temperature applications. The 310 family of steels all exhibit good properties at high temperatures combined with good ductility and weldability. Typical applications include Oven linings, boiler baffles, kilns, lead pots, radiant tubes, annealing covers, saggers, burners, combustion tubes, refractory anchor bolts, fire box sheets, furnace components and other high temperature containers

Chemical Composition

	C	Mn	Ni	Si	Cr	S	P	Fe
Min %	–	–	19.00	–	24.00	–	–	Bal.
Max %	0.25	2.00	22.00	1.50	26.00	0.03	0.045	–
Other Elements

 

Mechanical Properties

	MPA	%
Tensile Strength.	515 min.
Yield Strength (0.2% offset)	205 min.
Elongation in 2” (50mm) or 4D		40
Reduction of Area, min
Hardness	95 HRB max

 

Alternative Designations

AISI 310    AMS 5577    AMS 5651    ASTM A167    ASTM A182    ASTM A213    ASTM A249    ASTM A276    ASTM A314    ASTM A358    ASTM A403    ASTM A409    ASTM A473    ASTM A479    ASTM A580    ASTM A632    DIN 1.4841    QQ S763    QQ S766    UNS S31000

The data contained in this publication is for informational purposes only and may be revised at any time without prior notice. The data is believed to be accurate and reliable, but Hague Fasteners Limited makes no representation or warranty of any kind (express or implied) and assumes no liability with respect to the accuracy or completeness of the information contained herein. Although the data is believed to be representative of the product, the actual characteristics or performance of the product may vary from what is shown in this publication. Nothing contained in this publication should be construed as guaranteeing the product for a particular use or application.